Hoʻolei / ninini ʻana i ka Sillimanite Production
ʻO ka pahu pahu Sillimanite lalo (HL-A-60 TB)
Loaʻa i nā huahana Sillimanite nā waiwai o ke kūpaʻa haʻalulu maikaʻi, ka ikaika kiʻekiʻe ma nā wela kiʻekiʻe a me ke kiʻekiʻe kiʻekiʻe. ʻO lākou nā mea nui i koho mua ʻia no nā kapuahi aniani, nā kapuahi hoʻomehana, nā kiln kemika a me nā kapuahi metallurgic.
Hōʻike Kimia & Kino
'ikamu | Nā ʻano hana |
Huina Kemika% | Al2O3: ≥60 |
SiO2: ≤38 | |
Fe2O3: ≤1.0 | |
Ke kino | Waiwai |
ʻIke ʻia ka Porosity% | ≤18 |
ʻOi aku ka nui (g/cm3) | ≥2.4 |
Puanu ikaika Mpa | ≥60 |
0.2Mpa Refractoriness Ma lalo o ka ukana T0.6 ℃ | ≥1500 |
Hoʻololi Linear mau ma ka hoʻomehana hou ʻana1500℃X2h (%) | ±0.1 |
ʻO ke kū ʻana o ka haʻalulu wela 100 ℃ nā pōʻai wai | ≥20 |
ʻO ka hoʻonui wela wela 1000 ℃ | 0.006 |
Palapala noi
Hoʻohana nui ʻia i loko o ka pahu pahu lalo 2nd a me 3th papa o ka M/E & W/E, ʻoi aku hoʻi i ka Tableware Glass and Bottle Glass Furnace. Hoʻopau i nā kapuahi ahi a me ke kapuahi Kea etc.
'ikamu | A-60TB | SM-65 |
Al2O3 (%) | ≥60 | ≥65 |
Fe2O3 (%) | ≤1.3 | ≤1.0 |
ʻO ka refractoriness ℃ | ≥1750 | ≥1770 |
0.2Mpa Refractoriness Ma lalo o ka ukana T0.6 ℃ | ≥1550 | ≥1600 |
ʻIkepili Porosity % | ≤18 | ≤16 |
ʻOi aku ka nui (g/cm3) | ≥2.4 | ≥2.45 |
ʻO ka ikaika hoʻoheheʻe anuanu (Mpa) | ≥60 | ≥80 |
ʻO ke kūpaʻa haʻalulu wela 1100 ℃ Nā pōʻai wai | ≥20 | ≥15 |
Pono
- Hoʻonui i ka Durability: ʻO ke kaʻina hana hoʻolei haʻalulu e hoʻonui nui i ke ola o nā poloka ma lalo o nā kūlana paʻakikī.
- Hoʻopaʻa Wela ʻoi aku ka maikaʻi: ʻO ke kiʻekiʻe kiʻekiʻe a me ka haʻahaʻa haʻahaʻa haʻahaʻa e hoʻomaikaʻi i ka ikehu o ka umu ma ka hoʻemi ʻana i ka nalowale o ka ikehu.
- Hoʻoponopono kiʻekiʻe: Hiki ke hoʻopili ʻia nā poloka e hoʻokō i nā pono kikoʻī o nā ʻāpana umu like ʻole.
Ma ke koho ʻana i nā poloka sillimanite vibrating cast, hiki i nā mea hana aniani ke hoʻomaikaʻi nui i ka hana a me ka pono o kā lākou mau umu, e hōʻoiaʻiʻo ana i ka hana aniani kiʻekiʻe ʻoiai e loaʻa ana ka maikaʻi o ka ikehu maikaʻi a me ka kūpaʻa hoʻonohonoho.