Nkedo/ịkwasa mmepụta Sillimanite
Ihe mgbochi nke tank Bottom Sillimanite (HL-A-60 TB)
Ngwaahịa Sillimanite nwere ihe dị mma nke na-eguzogide okpomọkụ dị mma, ike dị elu na okpomọkụ dị elu na njupụta dị elu. ha bụ ihe mbụ ahọpụtara maka ọkụ iko, ọkụ ọkụ, kemịkalụ kemịkalụ na ọkụ ọla.
Ngosipụta kemịkalụ & anụ ahụ
Ihe | Omume |
Ngwakọta kemịkalụ% | Al2O3: ≥60 |
SiO2: ≤38 | |
Fe2O3: ≤1.0 | |
Anụ ahụ | Uru |
Pụrịa Porosity | ≤18 |
Njupụta nnukwu (g/cm3) | ≥2.4 |
Ike na-akụpịa oyi Mpa | ≥60 |
0.2Mpa Refractoriness n'okpuru ibu T0.6 ℃ | ≥1500 |
Mgbanwe Linear Na-adịgide adịgide Na-ekpo ọkụ1500℃X2h (%) | ±0.1 |
Thermal Shock Resistances 100 ℃ mmiri okirikiri | ≥20 |
Ọnụego Mgbasawanye okpomọkụ 1000 ℃ | 0,006 |
Ngwa
A na-ejikarị na tank ala 2nd na 3th layers nke M / E & W / E, karịsịa na Tebụlware Glass na Bottle Glass Furnace. Akwụsị ọkụ ọkụ na ọkụ cross-fire wdg.
Ihe | A-60TB | SM-65 |
Al2O3 (%) | ≥60 | ≥65 |
Fe2O3 (%) | ≤1.3 | ≤1.0 |
Refractoriness ℃ | ≥1750 | 1770 |
0.2Mpa Refractoriness n'okpuru ibu T0.6 ℃ | ≥1550 | ≥1600 |
Prọsity pụtara % | ≤18 | ≤16 |
Njupụta nnukwu (g/cm3) | ≥2.4 | ≥2.45 |
Ike Nchicha oyi (Mpa) | ≥60 | ≥80 |
Thermal Shock Stability 1100 ℃ okirikiri mmiri | ≥20 | ≥15 |
Uru
- Ọdịnaya emelitere: Usoro nkedo na-ama jijiji na-abawanye nke ukwuu ogologo ndụ nke ngọngọ n'okpuru ọnọdụ ọjọọ.
- Njide okpomoku kacha elu: Njupụta dị elu na ikuku ọkụ dị ala na-eme ka ike ọkụ ọkụ dị mma site na ibelata mfu ume.
- Nhazi dị elu: Enwere ike ịhazi ihe mgbochi iji gboo mkpa dị iche iche nke ngwa ọkụ dị iche iche.
Site n'ịhọrọ ihe nkedo sillimanite na-ama jijiji, ndị na-emepụta iko nwere ike ịkwalite arụmọrụ na ịdị mma nke ọkụ ha, na-ahụ na mmepụta iko dị elu ma na-enweta ezigbo ume ike na nguzosi ike n'ezi ihe.