Corundum Bricks-Hengli
Atụmatụ
Brick Corundum, nke a makwaara dị ka brik alumina, bụ ngwaahịa na-eme ka alumina dị elu nwere ọtụtụ atụmatụ dị mkpa:
1. **Elu Ọcha: **Ihe mejupụtara nke ihe karịrị 90% alumina (Al2O3), na-eme ka ihe nrụpụta dị mma.
2. ** Nguzogide oke okpomọkụ: **Nwere ike iguzogide okpomọkụ ruo 1900 Celsius, na-eme ka ha dị mma maka gburugburu ebe okpomọkụ dị elu na-achọsi ike.
3. ** Ike Mechanical: **Brick Corundum nwere ike mkpakọ dị elu na nguzogide dị mma, na-enyere ha aka ijikwa ibu dị arọ na ọnọdụ abrasive.
4. ** Nguzogide corrosion: **Ha na-eguzogide corrosion sitere na slags, acids, alkalis, na kemịkalụ ndị ọzọ, na-agbatị ndụ ha na gburugburu ebe siri ike.
5. ** Obere Ike: **Porosity dị ala na-enyere aka igbochi ntinye nke ihe ndị a wụrụ awụ na gas, na-eme ka ịdịte aka na ihe mkpuchi ọkụ.
6. ** Nkwụsi ike nke okpomọkụ: **Ha na-egosipụta nkwụsi ike dị mma na nguzogide okpomọkụ, nke dị oke mkpa maka usoro metụtara mgbanwe okpomọkụ ngwa ngwa.
7. ** Nkwụsi ike akụkụ: **Ọdịnaya alumina dị elu na-eme ka brik ahụ na-edobe ọdịdị ha na olu ha na oke okpomọkụ, na-egbochi ọdịda nhazi.
Atụmatụ ndị a na-eme ka brik corundum dị mma maka ojiji na ngwa dị elu dị elu, gụnyere ọkụ ọkụ, stovu na-ekpo ọkụ ọkụ, ladles ígwè, na ọkụ ọkụ ndị ọzọ na-arụ ọrụ na kilns.
Ngwa a na-ahụkarị
A na-ejikarị ya eme ihe na ụlọ ọrụ dị ka fatịlaịza, ceramics electrochemical, petrochemical, steel, foundry, alloy steel, refractories, wdg. Ngwa a na-ahụkarị dị ka onye na-eme mgbanwe nke abụọ na gas generator lining, catalyst bed support, channel induction oven, reheating oven hearth, wdg.
Ndekọ ahụkarị
Ọkwa | HA-99 | HA-98 | HA-90 | HA-80 | |
AI2O3 | % | ≥97.5 | ≥97 | ≥90 | ≥80 |
SiO2 | % | ≤0.18 | ≤0.2 | ≤8.5 | ≤18.5 |
Fe2O3 | % | ≤0.05 | ≤0.1 | ≤0.2 | ≤0.3 |
Njupụta nnukwu | g/cm3 | ≥3.15 | ≥3.1 | ≥3.1 | ≥2.9 |
Porosity pụtara | % | ≤16 | ≤17 | ≤18 | ≤18 |
Ike Nchicha oyi | MPa | ≥110 | ≥100 | ≥120 | ≥120 |
Refractoriness n'okpuru ibu (0.1 MPa, 0.6%) | Celsius C | ≥ 1700 | ≥ 1700 | ≥ 1700 | ≥ 1700 |
Mgbanwe Linear na-ekpo ọkụ (1600°C x8h) | % | ≥-0.2 | ≥-0.2 | ≤0.2 | ≤0.2 |
Ọnụọgụ mgbasawanye okpomọkụ x10-6 Okpomọkụ ime ụlọ. ruo 1300 ° C | 8.1 | 8.1 | 8.1 | 7.6 |