Ho Lahlela / Ho Tšela Tlhahiso ea Sillimanite
Tank Bottom Sillimanite Block (HL-A-60 TB)
Lihlahisoa tsa Sillimanite li na le thepa ea ho hanyetsa mocheso o motle oa mocheso, matla a phahameng a mocheso le mocheso o phahameng. ke lisebelisoa tsa pele tse khethiloeng tse phahameng bakeng sa libopi tsa khalase, libono tsa ho futhumatsa, libono tsa lik'hemik'hale le libono tsa metallurgic.
Letšoao la Lik'hemik'hale le 'Mele
Ntho | Boitšoaro |
Sebopeho sa Lik'hemik'hale% | Al2O3: ≥60 |
SiO2: ≤38 | |
Fe2O3: ≤1.0 | |
Ea nama | Boleng |
Ho bonahala Porosity | ≤18 |
Boima ba Bongata (g/cm3) | ≥2.4 |
Matla a Hatselang a batang Mpa | ≥60 |
0.2Mpa Refractoriness Under Load T0.6 ℃ | ≥1500 |
Phetoho e sa Feleng ea Linear On Reheating1500℃X2h (%) | ±0.1 |
Thermal Shock Resistances 100 ℃ potoloho ea metsi | ≥20 |
Sekhahla sa Katoloso ea Mocheso 1000℃ | 0.006 |
Kopo
Haholo-holo sebelisa bokatlase ba tanka 2nd le 3th layers tsa M/E & W/E, haholo-holo ho Tableware Glass le Bottle Glass Furnace. Likamore tsa mollo le libono tsa mollo oa Cross-fire joalo-joalo.
Ntho | A-60TB | SM-65 |
Al2O3 (%) | ≥60 | ≥65 |
Fe2O3 (%) | ≤1.3 | ≤1.0 |
Refractoriness ℃ | ≥1750 | ≥1770 |
0.2Mpa Refractoriness Under Load T0.6 ℃ | ≥1550 | ≥1600 |
Ho bonahala Porosity % | ≤18 | ≤16 |
Boima ba Bongata (g/cm3) | ≥2.4 | ≥2.45 |
Cold Crushing Strength (Mpa) | ≥60 | ≥80 |
Thermal Shock Stability 1100℃ Lipotoloho tsa metsi | ≥20 | ≥15 |
Melemo
- Tšireletseho e Ntlafetseng: Ts'ebetso ea ho thothomela e eketsa haholo nako ea bophelo ea li-blocks tlas'a maemo a thata.
- Tšireletso e Phahameng ea Mocheso: Boima bo phahameng le mocheso o tlase oa mocheso o ntlafatsa matla a sebōpi ka ho fokotsa tahlehelo ea matla.
- Tloaelo e phahameng: Li-block li ka etsoa ho fihlela litlhoko tse ikhethang tsa likarolo tse fapaneng tsa sebōpi.
Ka ho khetha li-block tsa sillimanite tse thothomelang, baetsi ba likhalase ba ka ntlafatsa haholo ts'ebetso le katleho ea libopi tsa bona, ba netefatsa tlhahiso ea likhalase tsa boleng bo holimo ha ba ntse ba fihlela ts'ebetso e nepahetseng ea matla le bots'epehi ba sebopeho.