Iibhloko eziphakamileyo ze-alumina ezikhuselayo zizinto ezikhethekileyo ezinqabileyo ezisetyenziswa kwizicelo ezahlukeneyo zobushushu obuphezulu ngenxa yeempawu zazo ezizodwa. Ezinye izinto eziphambili zeebhloko eziphezulu ze-alumina insulating ziquka:
1. I-Thermal Insulation: Zine-conductivity ephantsi ye-thermal, ezenza ukuba zisebenze kakhulu ekunciphiseni ukulahleka kobushushu kunye nokugcina ubushushu obuphezulu kwiziko kunye neekoni.
2. Amandla omatshini: Babonisa amandla afanelekileyo omatshini kunye nokuchasana ne-abrasion, okuqinisekisa ukuhlala kunye nokuphila ixesha elide kwiimeko ezinzima.
3. I-Lightweight: Nangona amandla abo kunye nokuqina, iibhloko eziphezulu ze-alumina insulating zilula, nto leyo eyenza kube lula ukuphatha nokufaka.
4. Ukuzinza kwe-Dimensional: Bagcina imilo yabo kunye nokunyaniseka kwesakhiwo phantsi kweemeko eziphezulu zokushisa, ukunciphisa i-deformation kunye nokuqhekeka.
5. Ukuphumelela kwamandla: Ngokubonelela nge-insulation egqwesileyo, ezi zibhloko zinceda ekugcineni amandla kunye nokunciphisa iindleko zokusebenza kwiinkqubo eziphezulu zokushisa.
Usetyenziso oluqhelekileyo
"IVibration Cast Fireclay Block yeGlass Furnace" iqhele ukusetyenziselwa ukugquma emazantsi nasezindongeni zeziko leglasi. Ezi zitena ze-fireclay azigcini nje ngokukhusela ngokufanelekileyo, ukuthintela ukusasazeka kwangaphandle kobushushu kunye nokugcina indawo ezinzileyo yobushushu obuphezulu ngaphakathi kwesithando somlilo seglasi, kodwa kunye neempawu zamandla aphezulu. Inkqubo yabo ekhethekileyo yokuphosa i-vibration inika ezi zitena ubuninzi obufanayo kunye nokusebenza kakuhle kwe-refractory, okubenza bakwazi ukumelana namaqondo okushisa aphezulu kunye neempembelelo eziveliswa ngexesha lokusebenza kweglasi yesithando somlilo, ukuqinisekisa ukuzinza kunye nokuthembeka ngexesha lokusebenza kwexesha elide.
Iizalathisi eziqhelekileyo
Izinto | I-FLG-1.2 | FLG-1.0 | FLG-0.8 | I-FLG-0.7 | FLG-0.6 | |
Al2O3 | % | ≥ 48 | ≥ 48 | ≥ 48 | ≥ 48 | ≥ 48 |
Fe2O3 | % | ≤ 2.0 | ≤ 2.0 | ≤ 2.0 | ≤ 2.0 | ≤ 2.0 |
Unizi lolwapho kuyiwa khona | g/cm3 | 1.2-1.3 | 1 | 0.8 | 0.7 | 0.6 |
Amandla okutyumza okubandayo | MPa | 15 | 4 | 3 | 2.5 | 2 |
Ukufudumeza umgca wokutshintsha kwakhona akukho ngaphezu kwe-2% | % | 1400 | 1400 | 1400 | 1350 | 1350 |
I-Thermal Conductivity @350 ± 10°C | W/m·K | 0.55 | 0.5 | 0.35 | 0.35 | 0.3 |