Izangqa zeOrifice zeglasi eshushu yokuphela
Iimbonakalo
95% corundum/99.7% corundum
Iringi ye-orifice ene-oxide ceramic efakwe kubavelisi beglasi yokupakisha yaphuhliswa yi-HENGLI kwiminyaka emininzi eyadlulayo.
Bayanda nangakumbi abenzi beglasi abazinikele kwi-LONG-PRODUCTION RUN ukuba bavelisa isikhongozeli esinye esingayekiyo.
Izisombululo ezininzi zobugcisa kunye noqoqosho olungaphantsi okanye oluxabisa kakhulu lokufaka isisombululo ekhoyo kwimarike.
Isicelo
Ixabiso elicacileyo, elongeziweyo lezi zisombululo zenziwe nge-HENGLI ziqinisekiswa ngabenzi beglasi abaninzi kuquka onke amaQela aMazwe ngaMazwe kwi-Glass Packaging afumana ukonga okukhulu ngokwenene nge-spam yobomi iintsuku ezingama-70-150 ngokuxhomekeke kwiqondo lobushushu kunye nesantya sokutsala ngakumbi kwi-DG/ TG.
Eyona nto iluncedo kakhulu kolu fakelo lweringi yeOrifice ayinayo i-decolorization nakwi-flint kunye neglasi eyongezelelekileyo kwaphela.
Iinketho zexesha elide:I-88% ye-zircon-corundum / i-95% ephezulu-zirconia.
I-HENGLI-isostatic icinezelwe iinketho ezifakelweyo nokuba zezekeramics ezisekelwe kwialumina eziphezulu ezinomatshini ofanelekileyo okanye ukuphuhlisa isisombululo esitsha esinezisombululo eziphezulu ze-alumina-zirconia (iprojekthi yokulinga), eya kuthi inike ubomi obude bogaxekile, kodwa inokumelana nokothuka kwe-thermal.
Imichiza kunye neDatha yoMzimba
Umsesane we-Orifice Z20-CFP | |
UHLELO LWEKHEMICAL % | |
AL203[%] | 67 |
Zr0 [%] | 20 |
Si0 [%] | 12 |
Fe203[%] | 0,1 |
Na0[%] | 0,2 |
Ti02[%] | 0,1 |
IIPARAMETHA ZOMZIMBA | |
Uxinzelelo olubonakalayo [g/cm"] | 2,65 |
Amandla okutyumza okubandayo [N/mm] | 50 |
I-porosity evulekileyo [%] | 29 |
Ukwandiswa kweThermal kwi-1000 ℃: | 0,7 |
Umda wobushushu besicelo ℃: |