Ukukhiqiza/Ukuthulula I-Sillimanite Production
I-Tank Bottom Sillimanite Block (HL-A-60 TB)
Imikhiqizo ye-Sillimanite inezakhiwo zokumelana nokushaqeka okuhle kokushisa, amandla aphezulu emazingeni okushisa aphezulu kanye nokuminyana okuphezulu. ziyizinto zokuqala ezikhethiwe ezisezingeni eliphezulu zeziko lengilazi, iziko lokufudumeza, iziko lamakhemikhali kanye neziko le-metallurgic.
I-Chemical & Physical Inkomba
Into | Ukuziphatha |
Ukwakheka Kwekhemikhali% | I-Al2O3: ≥60 |
I-SiO2: ≤38 | |
I-Fe2O3: ≤1.0 | |
Okomzimba | Inani |
I-Porosity ebonakalayo. | ≤18 |
Ukuminyana kwenqwaba (g/cm3) | ≥2.4 |
Amandla Okuchotshozwa Okubandayo Mpa | ≥60 |
0.2Mpa Refractoriness Under Load T0.6 ℃ | ≥1500 |
Ushintsho Lomugqa Ongunaphakade Ekushiseni kabusha1500℃X2h (%) | ±0.1 |
I-Thermal Shock Resistances 100℃ imijikelezo yamanzi | ≥20 |
I-Thermal Expansion Rate 1000℃ | 0.006 |
Isicelo
Ngokuyinhloko sebenzisa ethangini ngezansi izendlalelo zesi-2 no-3 ze-M/E & W/E, ikakhulukazi ku-Tableware Glass kanye ne-Bottle Glass Furnace. Qeda iziko lomlilo kanye neCross-fire furnace njll.
Into | A-60TB | I-SM-65 |
I-Al2O3 (%) | ≥60 | ≥65 |
I-Fe2O3 (%) | ≤1.3 | ≤1.0 |
I-Refractoriness ℃ | ≥1750 | ≥1770 |
0.2Mpa Refractoriness Under Load T0.6 ℃ | ≥1550 | ≥1600 |
I-Porosity ebonakalayo % | ≤18 | ≤16 |
Ukuminyana kwenqwaba (g/cm3) | ≥2.4 | ≥2.45 |
Amandla Okuchotshozwa Okubandayo (Mpa) | ≥60 | ≥80 |
I-Thermal Shock Stability 1100℃ Imijikelezo yamanzi | ≥20 | ≥15 |
Izinzuzo
- Ukuqina Okuthuthukisiwe: Inqubo yokulingisa edlidlizayo yandisa kakhulu isikhathi sokuphila samabhulokhi ngaphansi kwezimo ezinzima.
- Ukugcina Ukushisa Okuphakeme: Ukuminyana okuphezulu kanye nokuhanjiswa kwe-thermal okuphansi kuthuthukisa ukusebenza kahle kwesithando somlilo ngokunciphisa ukulahleka kwamandla.
- Ukwenza Ngokwezifiso Okuphezulu: Amabhulokhi angalungiswa ukuze ahlangabezane nezidingo ezithile zezingxenye ezihlukene zesithando somlilo.
Ngokukhetha amabhlogo we-cast sillimanite adlidlizayo, abakhiqizi bezingilazi bangathuthukisa kakhulu ukusebenza nokusebenza kahle kwezithando zabo, baqinisekise ukukhiqizwa kwengilazi yekhwalithi ephezulu kuyilapho bezuza ukusebenza kahle kwamandla nobuqotho besakhiwo.