Izindandatho ze-Orifice ze-Glass Hot End
Izici
95% corundum/99.7% corundum
Indandatho ye-orifice ene-oxide ceramic insert yabakhiqizi bezingilazi zokupakisha yakhiwe yi-HENGLI eminyakeni eminingi edlule.
Bayanda abenzi bezingilazi abazinikele ku-LONG-PRODUCTION RUN uma bekhiqiza isiqukathi esifanayo ngokungami.
Izixazululo eziningana zobuchwepheshe kanye nezixazululo zokufaka ezongayo ezingaphansi noma ezibiza kakhulu ezikhona emakethe.
Isicelo
Inani elicacile, elengeziwe lalezi zixazululo ezenziwe nge-HENGLI liqinisekiswa abenzi bezingilazi abaningi okuhlanganisa nawo wonke Amaqembu Amazwe Ngamazwe Ku-Glass Packaging athola ukonga okukhulu ngempela ngogaxekile bokuphila izinsuku ezingama-70-150 kuye ngezinga lokushisa kanye nezinga lokudonsa ikakhulukazi ku-DG/ TG.
Inzuzo engcono kakhulu yalokhu kufakwa kwendandatho ye-Orifice engenakho ukuhlukaniswa kombala ngisho nengilazi yetshe letshezela eyengeziwe.
Izinketho zesikhathi eside:I-88% ye-zircon-corundum / i-95% ephezulu-zirconia.
Izinketho ezifakiwe ze-HENGLI-isostatic ezicindezelwe kungaba izitsha zobumba ezisekelwe ku-alumina eziphezulu ezinomshini ofanele noma ukuthuthukisa isixazululo esisha esinezixazululo ze-alumina-zirconia eziphezulu (iphrojekthi yokuhlola), ezonikeza ugaxekile wempilo ende, kodwa ibe nokumelana nokushaqeka okuphansi uma kuqhathaniswa.
Idatha Yekhemikhali Neyomzimba
Indandatho ye-Orifice Z20-CFP | |
UKWAKHIWA KWEKHEMICAL % | |
AL203[%] | 67 |
Zr0 [%] | 20 |
Si0 [%] | 12 |
Fe203[%] | 0,1 |
Na0[%] | 0,2 |
Ti02[%] | 0,1 |
AMAPHYSICAL PARAMETERS | |
Ukuminyana okubonakalayo [g/cm"] | 2,65 |
Amandla okuchoboza abandayo [N/mm] | 50 |
I-porosity evulekile [%] | 29 |
Ukunwetshwa kwe-Thermal ku-1000 ℃: | 0,7 |
Umkhawulo wokushisa wohlelo lokusebenza ℃: |